Zirconia Laserdenta YZ
Made in Germany CE/FDA
| Article-No. | Description | |
| A401402 | Zirconia Ø 98 x 14 mm VITA In-Ceram YZ Disc for Laserdenta |
 |
| A401404 | Zirconia Ø 98 x 18 mm VITA In-Ceram YZ Disc for Laserdenta |
|
| A401405 | Zirconia Ø 98 x 20 mm VITA In-Ceram YZ Disc for Laserdenta |
|
Physical data
| Density | > 6,05 g/m³ |
| Bending strength | > 900 MPa |
| E-Modul |
210 GPa |
| Thermal expansion | 10,5 10-6 K-1 |
| Chemical solubility | <20 µg/cm² |
| Vickershardness | 1200 HV |
Sintering program
| Fire | 120 Min. to 1530 degrees |
| Hold | 120 Min. at 1530 degrees |
| End | cool down in furnace to 400 degrees |
| Shrinkage factor | siehe disc |
Zirconia colored, A2/A3/C3/B4/A4
Made in Germany CE/FDA
| Article-No. | Color | Description | |
| A500010 A500018 A500026 A500034 A500042 |
A2 A3 C3 B4 A4 |
Zirconia Ø 98 x 14 mm BIOStar-Zirkon Disc 98 ø x 14 mm | |
| A500012 A500020 A500028 A500036 A500044 |
A2 A3 C3 B4 A4 |
Zirconia Ø 98 x 18 mm BIOStar-Zirkon Disc 98 ø x 18 mm | |
| A500014 A500022 A500030 A500038 A500046 |
A2 A3 C3 B4 A4 |
Zirconia Ø 98 x 20 mm BIOStar-Zirkon Disc 98 ø x 20 mm | |
| A500016 A500024 A500032 A500040 A500048 |
A2 A3 C3 B4 A4 |
Zirconia Ø 98 x 25 mm BIOStar-Zirkon Disc 98 ø x 25 mm | |
Physical data
| Density | > 6,05 g/m³ |
| Bending strength | > 1000 +/- 200 MPa |
| E-Modul | 210 GPa |
| Thermal expansion | 10,5 10-6 K-1 |
| Chemical solubility | <1 µg/cm2 DIN EN ISO 10903/6872 |
Sintering program
| Single crown |
3-4 unit bridges |
Bridges > 4units | |
| Fire to 900° | 59 min | 73 min | 110 min |
| Hold at 900° | 5 min | 15 min | 30 min |
| Fire to 1450° | 36 min |
46 min | 69 min |
| Hold at 1450° | 30 min | 120 min | 120 min |
| Fire to 900° | 55 min | 110 min | 138 min |
| Hold at 900° | 5 min | 10 min | 20 min |
| Cool down to 200° | 70 min | 135 min | 175 min |
Zirconia white, translucent
Made in Germany CE/FDA
| Article-No. | Color | Description | |
| A500048 A500049 A500050 A500051 A500052 A500053 A500054 A500055 |
10mm 12mm 14mm 16mm 18mm 20mm 22mm 25mm |
Zirconia Ø 98 mm BIOStar-Zirkon Disc white, translucent 98 ø mm | |
Sintering program
| Single crown |
3-4 unit bridges |
Bridges > 4units | |
| Fire to 900° | 59 min | 73 min | 110 min |
| Hold at 900° | 5 min | 15 min | 30 min |
| Fire to 1500° | 40 min |
50 min | 75 min |
| Hold at 1500° | 120 min | 120 min | 120 min |
| Fire to 900° | 60 min | 120 min | 150 min |
| Hold at 900° | 5 min | 10 min | 20 min |
| Cool down to 200° | 70 min | 135 min | 175 min |